BND 20 30 – petroleum bitumen road with a penetration index of 20-35 mm, which belongs to the class of viscous road compounds.
The main purpose of BND 20 30 bitumen is the construction and repair of roadways. In addition, the composition of viscous petroleum bitumen can be used as the main component in the production of modified bitumen and bitumen emulsions.
The composition should be applied at an ambient temperature of at least +5 ° C. Bitumen BND 20/35 is laid on the surface in a preheated state to +160 ° C. The surface on which the composition will be laid must be clean and dry. If the surface area to be treated is large, bitumen is applied using fillers. When processing small areas, it is recommended to use brushes or rollers..
Specifications

• Needle penetration depth at +25 °C is 20-35 mm
• The penetration depth of the needle at 0 ° C is not less than 10 mm
• The change in the mass of the sample after aging is not more than 0.5%
• The change in softening temperature after aging is no more than 6 ° C.
• Penetration index from -1.0 to +1.0
• Solubility not less than 99%
• Stretchability at +25 ° C is not less than 40 cm
• Extensibility at 0 °C is not determined
• The content of solid paraffins is not more than 3.0%
• Flash point not lower than +230 °C
• The softening temperature in KISH is not lower than + 55 °C.
• The brittleness temperature is not higher than -11 °C.
• The temperature of brittleness after aging is not higher than -8 °C.

Bitumen BND 35-50 is a homogeneous compound made by distillation of petroleum products and intended for road construction.
Bitumen 35-50 is used during repair and construction work on roadways. With its help, waterproofing of road surfaces is carried out, defects in the form of pits, potholes, seams and cracks are eliminated. In addition, the composition of BND 3550 is used as one of the main components in the production of modified bitumen and bitumen emulsions.
Bitumen BND 35 50 is a composition of "hot" application. The composition is laid after preheating the material to a temperature of +160 ° C, which is optimal. After that, bitumen is applied to the cleaned and dry road surface with the help of fillers. Fillers and scrapers are used to process a large area, and special construction brushes are recommended for waterproofing small coatings.
Specifications

• Needle penetration depth at +25 °C is 36-50 mm
• The penetration depth of the needle at 0 ° C is not less than 14 mm
• The change in the mass of the sample after aging is not more than 0.5%
• The change in softening temperature after aging is no more than 6 ° C.
• Penetration index from -1.0 to +1.0
• Solubility not less than 99% +
• Stretchability at +25 ° C is not less than 50 cm
• Extensibility at 0 °C is not determined
• The content of solid paraffins is not more than 3.0%
• Flash point not lower than +230 °C
• The softening temperature in KISH is not lower than + 53 °C.
• The brittleness temperature of the mastic layer is not higher than -14 °C.
• The temperature of brittleness after aging is not higher than -11 °C.

BND 40 60 is petroleum bitumen with a penetration index at +25 ° C from 40 to 60 mm.
Bitumen BND 40 60 is produced according to GOST 22245-90, which defines that the composition of viscous petroleum bitumen is used as a binder in the construction of road surfaces and airfield tracks. It provides high-quality waterproofing, eliminates seams, cracks, potholes and pits that interfere with the normal and safe operation of highways and runways.
Bitumen road BND 40 60 is heated to a temperature of no more than +200 ° C before use (+ 220 ° C is the flash point of the composition). The work surface is pre-cleaned and dried. After that, with the help of fillers or brushes, the composition is laid.
Specifications

• Needle penetration depth at +25 °C is 40-60 mm
• The penetration depth of the needle at 0 ° C is not less than 13 mm
• The softening temperature change after heating is no more than 5 ° C.
• Penetration index from - 1.0 to +1.0
• Stretchability at +25°C 45 cm
• Extensibility at 0 °C no indicator
• Flash point not lower than +230 °C
• The softening temperature in KISH is not lower than + 51 °C.
• The brittleness temperature is not higher than -12 °C.

BND 50 70 is petroleum bitumen with a penetration index of 50-70 mm, which is intended for repair and installation of road surfaces, elimination of defects on road and airfield tracks, as well as for the production of bitumen and bitumen emulsions.
Bitumen BND 50 70 GOST 33133-2014 is preheated before carrying out waterproofing work. The composition is melted in boilers to a temperature of no more than + 200 ° C (at + 220 °With the composition ignites). During the heating process, it is recommended to stir the bitumen to avoid lumps and clots. The composition is applied to the surface, which has been previously cleaned and dried. It is recommended to use brushes and rollers to lay the composition of BND 50 70 if the surface to be treated has a small area. If the treated area has significant dimensions, then automated fillers and scrapers should be used, which allow high-quality waterproofing of large-area coatings.
Specifications

• Needle penetration depth at +25 °C is 51-70 mm +
• The penetration depth of the needle at 0 ° C is not less than 18 mm
• The change in the mass of the sample after aging is not more than 0.6%
• The change in softening temperature after aging is no more than 7 ° C.
• Penetration index from -1.0 to +1.0
• Solubility not less than 99%
• Stretchability at +25 ° C is not less than 60 cm
• Extensibility at 0 ° C is not less than 3.5 cm
• , the content of solid paraffins is not more than 3.0%
• Flash point not lower than +230 °C
• The softening temperature in KISH is not lower than + 51 °C.
• The brittleness temperature is not higher than -16 °C.
• The temperature of brittleness after aging is not higher than -13 °C.

Bitumen BND 60 90 is a viscous composition of the "hot" type of application, which has a penetration index of 60-90 mm and is intended for road construction.
Specifications

• Needle penetration depth at +25 °C is 61-90 mm
• The penetration depth of the needle at 0 ° C is not less than 20 mm
• The softening temperature change after heating is no more than 5 ° C.
• Penetration index from - 1.0 to +1.0
• Stretchability at +25°C 55 cm
• Stretchability at 0 °C 3.5 cm
• Flash point not lower than +230 °C
• The softening temperature in KISH is not lower than + 47 °C.
• The brittleness temperature is not higher than -15 °C.

Bitumen BND 70 100 is a viscous petroleum road composition manufactured according to GOST 33133-2014 and having a penetration index in the range from 70 to 100 mm.
Bitumen road BND 70 100 is a compound that is designed for waterproofing roadways. With its help, work is carried out to eliminate cracks, seams, as well as potholes and pits that interfere with the normal operation of road and airfield tracks. In addition, BND 70 100 is used as a binder in the production of modified bitumen and bitumen emulsions.
Before laying, bitumen petroleum road BND 70 100 is heated at a temperature of no more than +200 ° C (at +220 °The composition flashes). The work surface to be treated is pre-cleaned, primed and dried. After that, bitumen is laid on the surface using a brush, roller or fillers.
Specifications

• Needle penetration depth at +25 °C 71-100 mm
• The penetration depth of the needle at 0 ° C is not less than 21 mm
• The change in the mass of the sample after aging is not more than 0.7%
• The change in softening temperature after aging is no more than 7 ° C.
• Penetration index from -1.0 to +1.0
• Solubility not less than 99%
• Stretchability at +25 ° C is not less than 62 cm
• Stretchability at 0 °C is not less than 3.7 cm
• The content of solid paraffins is not more than 3.0%
• Flash point not lower than +230 °C
• The softening temperature in KISH is not lower than + 47 °C.
• The brittleness temperature is not higher than -18 °C.
• The temperature of brittleness after aging is not higher than -15 °C.

Bitumen BND 90 130 is a viscous petroleum product manufactured in accordance with GOST 22245-90 and intended for repair and construction work on road and airfield surfaces.
Bitumen viscous BND 90 130 is a compound that is placed on the work surface in a heated form. The permissible heating temperature should not exceed +200 °C, because at +220 °The composition flares up, and at +368 ° C bitumen ignites. The substrate to be waterproofing must be cleaned and primed. After that, using brushes, a roller, fillers or construction watering cans, the composition is applied to the prepared surface. All work with BND 90 130 is recommended to be carried out in personal protective equipment to prevent hot bitumen from getting on the skin.
Specifications

• Needle penetration depth at +25 °C 91-130 mm
• The penetration depth of the needle at 0 ° C is not less than 28 mm
• The softening temperature change after heating is no more than +5 °With
• Penetration index from - 1.0 to +1.0
• Stretchability at +25°C is 65 cm
• Stretchability at 0 °C 4.0 cm
• Flash point not lower than +220 °C
• The softening temperature in KISH is not lower than + 43 °C.
• The brittleness temperature is not higher than -17 °C.

Bitumen BND 100 130 refers to compositions for "hot" laying. With its help, it is possible to create a high-strength waterproofing coating, which is distinguished not only by its wear resistance, but also by its ability to prevent deformations, corrosion and other negative impacts from outside, which can adversely affect the operation of highways. In addition, the viscous composition is used as one of the components intended for the creation of modified bitumen and bitumen emulsions.
Bitumen petroleum road BND 100 130 is a compound that needs to be preheated. The material is laid after it has acquired a fluid consistency. For this purpose, special boilers are used that allow you to heat bitumen BND 100 130, which can be purchased on our website, to the optimal viscosity level. After the composition has acquired the necessary consistency, it is applied to the surface with brushes, roller or fillers, which is cleaned and dried.
Bitumen consumption depends on the type of work, the thickness of the coating layer, as well as the structure of the base material and averages about 6-8 kg per 1 sq.m.
Specifications

• Needle penetration depth at +25 °C 101-130 mm
• The penetration depth of the needle at 0 ° C is not less than 30 mm
• The change in the mass of the sample after aging is not more than 0.7% +
• The change in softening temperature after aging is no more than 7 ° C.
• Penetration index from -1.0 to +1.0
• Solubility not less than 99%
• Stretchability at +25 ° C is not less than 70 cm
• Stretchability at 0 °C is not less than 4.0 cm
• The content of solid paraffins is not more than 3.0%
• Flash point not lower than +230 °C
• The softening temperature in KISH is not lower than +45 °C.
• The brittleness temperature is not higher than -20 °C.
• The temperature of brittleness after aging is not higher than -17 °C.

Externally, bitumen BND 130 200 is a viscous homogeneous composition, which is produced by oxidation of products of direct distillation of petroleum and petroleum products.
Bitumen petroleum road BND 130 200 is applied to a cleaned and dry surface in a heated form. For high-quality softening of the composition, it is recommended to use special boilers that allow the composition to be brought to an optimal state, which will allow the composition to be laid on a prepared working base.
Specifications

• Needle penetration depth at +25 °C is 131-200 mm
• The penetration depth of the needle at 0 ° C is not less than 40 mm
• The change in the mass of the sample after aging is not more than 0.8%
• The change in softening temperature after aging is no more than +7 °With
• Penetration index from -1.0 to +1.0
• Solubility not less than 99%
• Stretchability at +25 ° C is not less than 80 cm
• Stretchability at 0 °C is not less than 6.0 cm
• The content of solid paraffins is not more than 3.0%
• Flash point not lower than +220 °C
• The softening temperature in KISH is not lower than +42 °C.
• The brittleness temperature is not higher than -21 °C.
• The temperature of brittleness after aging is not higher than -18 °C.

The composition of BND 200 300 is in demand during the construction and repair of road surfaces and airfield tracks, and the composition is also used as the basis for the production of modified bitumen and bitumen emulsions.
Specifications

• Needle penetration depth at +25 °C 201-300 mm
• The penetration depth of the needle at 0 ° C is not less than 45 mm
• The softening temperature change after heating is no more than 7 ° C.
• Penetration index from - 1.0 to +1.0
• Extensibility at +25 ° C is not an indicator
• The stretchability at 0 °C is 20 cm
• Flash point not lower than +220 °C
• The softening temperature in KISH is not lower than + 35 °C.
• The brittleness temperature is not higher than -20 °C.

Bitumen BN 60 90 is used as a binder in the construction and repair of road and airfield surfaces, as well as in the production of mastics, waterproofing and roofing materials, materials for processing foundations and pipelines.
Bitumen BN 60 90 is used in hot form. Before use, the composition is heated at a temperature from +180 ° C to +190 ° C. After that, the heated composition is placed on a surface that has been previously cleaned and dried.
Specifications

• Needle penetration depth at +25 °C from 60 to 90 mm
• The penetration depth of the needle at 0 ° C is not less than 10 mm
• The change in the warm-up temperature after warming up is no more than 6 ° C.
• The penetration index is from - 1.5 to +1.0
• Stretchability at +25°C 70 cm
• Flash point not lower than + 240°C
• The softening temperature in KISH is not lower than + 45 °C.
• The brittleness temperature is not higher than -6 °C.

Bitumen BN 90 130 is used during repair and construction works, it is distinguished by its ability to create high-quality road waterproofing and provide long-lasting protection of treated objects from corrosion and destruction.
BN 90 130 is used during repair and construction work on the foundations of airfield surfaces and roadways. The composition allows for high-quality waterproofing of bases, and is also used in the process of eliminating defects in the form of cracks, potholes and pits that interfere with the normal operation of highways and runways.
Bitumen BN 90 130 is used in a heated form. The permissible heating temperature should not be around +190 °C. At +220°The composition flares up, and at +368 ° C it self-ignites, therefore, compliance with temperature ranges is very important when working with the composition. After the bitumen has reached the desired consistency, it is laid on a pre-cleaned work base.
Specifications

• Needle penetration depth at +25 °C 91-130 mm
• The penetration depth of the needle at 0 ° C is not less than 15 mm
• The change in the warm-up temperature after warming up is no more than 6 ° C.
• Penetration index from -1.5 to +1.0
• Stretchability at +25 °C 80 cm
• Flash point not lower than +240°C
• The softening temperature in KISH is not lower than + 41°With
• The brittleness temperature is not higher than -10 °C.

Viscous road composition, which is used in the process of arranging roads and runways of airfields.
The main purpose of the composition of petroleum bitumen BN 130 200 is to carry out road construction works and the production of modified bitumen, as well as bitumen emulsion compositions. In addition, petroleum bitumen road BN 130 200 is used as a composition for surface treatment of coatings in areas with a temperate climate, for impregnation of crushed stone coatings in areas with cold and temperate climates.
Specifications

• Needle penetration depth at +25 °C is not less than 131-200 mm
• The penetration depth of the needle at 0 ° C is not less than 18 mm
• The change in softening temperature after aging is not more than 7 °C.
• Penetration index from -1.5 to +1.0
• Stretchability at +25 ° C is not less than 80 cm
• Flash point not lower than +230°C
• The softening temperature in KISH is not lower than +38°C
• The brittleness temperature is not higher than -12°C

Bitumen BN 200 300 is a viscous petroleum composition with a penetration of 200-300 mm and is intended for various types of construction work in the field of road construction and materials production. The product is used as a binder in the construction and repair of road surfaces and foundations, as well as as a base for the production of modified bitumen and bitumen emulsions.
Bitumen road BN 200 300 is a compound designed for “hot” application. This means that the composition is heated to a liquid state before use. The work surface is pre-cleaned, primed and dried. Then the composition is laid on the prepared base. A layered application is recommended, which is done by using a wide brush or roller.
Bitumen consumption depends on the type of work, the thickness of the created layer and the structure of the material of the working area. On average, the material consumption is in the range of 6-8 kg per 1 sq.m.
Specifications

• Needle penetration depth at +25 °C 201-300 mm
• The penetration depth of the needle at 0 ° C is not less than 24 mm
• The change in softening temperature after aging is not more than 8 ° C.
• The penetration index is from -1.5 to 1.0
• Extensibility at +25 °C -
• Flash point not lower than +220 °C
• The softening temperature in KISH is not lower than + 33 °With
• The brittleness temperature is not higher than -14 °C.