Bitumen mastic for "hot" laying is one of the most popular waterproofing compounds, which allows you to create a high-quality and durable insulating coating.
Hot bitumen mastic is a mixture of petroleum bitumen and fillers of various types, the mixture of which forms a homogeneous mass intended for hot waterproofing.
Hot bitumen mastic, the price of which is favorable and affordable, has high adhesion to various surfaces, and is also endowed with the ability to create a durable and high-quality waterproofing coating with excellent protective functions and the ability to provide an adequate level of heat, moisture and vapor insulation. It is also worth noting that hot-applied mastic is endowed with excellent penetrating ability and has good adhesive properties.
The bitumen mastic is heated to a temperature of no more than +160 ° C before use. After that, the heated composition is applied to a pre-cleaned and primed surface. Note that the priming layer must dry, only after that the layer-by-layer waterproofing is carried out with a composition of hot mastic.
Specifications

• Flexibility at (18± 2)°C on a rod with a diameter of 10 mm
• Adhesion strength to the substrate is not less than 0.1 MPa
• Softening temperature in KISH from +55 °C to +60 °C
• Heat resistance for 5 hours at least +55 °C

Waterproofing concrete with bitumen mastic allows you to protect concrete surfaces from damage, moisture and external negative influences.
Bitumen mastic for concrete allows to provide high-quality heat and vapor insulation of concrete structures, as well as to protect concrete surfaces from deformations and premature destruction.
Bitumen mastic for concrete contains a resin-binding substance modified with technological additives and fillers. These components should form a homogeneous mixture that does not contain visible foreign inclusions.
Specifications

• excellent waterproofing, thermal insulation and vapor barrier properties;
• anti-corrosion resistance;
• resistance to deformation;
• resistance to moisture;
• optimal elasticity and plasticity, which facilitate the application of bitumen mastic to concrete;

Bitumen mastic is frost-resistant - it allows for proper insulation and protects objects, structures, structures and their elements from corrosion when operating at low temperatures.
It is designed to maintain an optimal level of insulation and protection of a variety of objects, surfaces, structures and structures that are in operation in a cold environment. In addition, the compound can be used during sealing of couplings and power cables, providing them with proper insulation.
Bitumen waterproofing mastic is mainly used in a heated form. At temperatures below + 5 ° C, the composition must be heated in a water bath or using burners, observing all fire safety rules. Then the composition is brought to an optimally flowing state, and then applied to the surface using a brush, roller or spatula.
Specifications

• Water absorption not more than 0.1%
• Drying time of the applied layer, at +20 ° C not more than 24 hours
• The test flexibility on the bar is 25 ± 0.2 mm, at t = -15 ° C no cracks
• Adhesion strength to the substrate 0.05 MPa
• Operating temperature range from -40°C to +45°C
• Heat resistance at +80 °C unchanged

Cold bitumen mastic allows you to quickly insulate the work surface and create an anti-corrosion barrier.
Cold-applied bitumen mastic is a compound designed for use without preheating, made by mixing petroleum bitumen with various fillers and additives.
Cold bitumen mastic is used as a compound that provides the creation of hydro and vapor barrier layers, and can also be used during roof construction and roofing.
Specifications

• Waterproof in 10 minutes at a pressure of at least 0.03 MPa
• Water absorption In 24 hours - no more than 2%
• Drying time "before sticking" is at least 48 hours at +20°C
• Flexibility on a 10 mm diameter rod at -5 °C
• Elongation at break of at least 100%
• Adhesion strength to the substrate is not less than 0.1 MPa
• Conditional strength of at least 0.2 MPa

Bitumen mastic is a "hot" roofing mastic, which is intended for the installation of roofs and the laying of roofing coverings.
It is a roofing compound made on the basis of bitumen binders and fillers, the mixing of which forms a homogeneous mass intended for "hot" application.
The functionality of mastic is based on roofing work. Thus, roofing mastic is intended for the construction of mastic and glass-reinforced roofs. In addition, the composition allows for optimal heat, steam, and waterproofing of roofs and roofing coverings.
Specifications

• Flexibility at (18± 2)°C on a rod with a diameter of 10 mm
• Adhesion strength to the substrate is 0.1MPa
• Softening temperature in KISH from +55 °C to +60 °C
• Heat resistance for 5 hours at least 55 ° C

MB 7060 mastic is designed to insulate cable couplings and protect them from mechanical damage.
Mastic MB 70 60 is a bitumen-petroleum composition having a drop point of +70 ° C and an average softening temperature of +60 ° C, which is intended for filling connecting, branch and end couplings, as well as power and control cables. The composition is a solid combustible substance that is heated to +160 ° C before use.
Mastic MB 70 60, which can be purchased on our company's website, is a compound that requires heating to +160 °C before being applied to the work surface. After the composition has acquired the consistency necessary for application, it is laid on a pre-cleaned work area. It is recommended to use a brush, roller or spray gun for application.
Specifications

• The pH of the water extract is not determined
• It can withstand the test of brittleness and adhesion to metals.
• Mass fraction of substances insoluble in toluene no
• Frost resistance is not higher than - 5 ° C.
• Breakdown voltage with alternating current for 1 min is not lower than 50,000 V
• Flash point from +170 °C to +220 °C
• The temperature of filling and heating the composition before use is +160 ° C.
• The softening temperature is from + 55 °C to +65 °C.
• Self-ignition temperature +368 °C
• Shrinkage is not more than 6.0%

MB 50 mastic is a frost-resistant compound made on the basis of petroleum bitumen and transformer oil, used for waterproofing various objects and structures in order to protect against breakdown of electrical networks and stray currents. In addition, the composition finds its application in the filling of connecting and end couplings.
Containing transformer oil, frost-resistant MB 50 mastic acquires not only excellent insulating and anti-corrosion properties, but also contributes to the creation of a coating that can be operated regardless of temperature fluctuations, without deforming or collapsing. The composition of the mastic is resistant to moisture, precipitation and corrosion.
The composition of the MB 50 mastic is applied to the cleaned and bordered surface in a preheated to +180 ° C. The application is carried out using a brush, roller or spray gun. The composition is applied in layers to obtain a high-quality coating that does not contain any gaps in the composition of the mastic.
Specifications

• Needle penetration depth at +25 °C 40 mm
• The mass fraction of substances insoluble in toluene is not more than 0.2%
• The mass fraction of soluble acids and alkalis is absent
• Frost resistance is not higher than -45 °C.
• Breakdown voltage with an alternating current of 50 Hz for 1 minute is not lower than 4000 V
• Flash point not lower than + 170 °C
• Heating temperature +180 ° C
• Softening temperature from +55 °C to +60 °C
• The operating temperature of the composition is not lower than -50 ° C.

Bitumen-rubber mastic allows you to create a high-quality waterproofing coating, designed to isolate objects of various types and purposes in order to create an anti-corrosion barrier, optimal protection from moisture and mechanical damage.
Bitumen rubber waterproofing mastic is a compound that does not require heating and special skills for its application. The composition is laid on the surface, which is cleaned, dried and treated with a primer. Apply the mastic to the dried primed coating using a brush, roller or spray gun. The choice of tool depends on the surface area to be treated.
Specifications

• Water absorption not more than 0.5% by weight
• Density at +20 °C 0.90 ± 10 g/cm3
• Heat resistance in 5 hours +75 ° C
• Conditional tensile strength of 0.4 kgf/m2
• Bending elasticity on a beam with a radius of 10 mm -15 ° C

BKM 100 mastic is a bitumen-rubber compound with excellent insulating functions, ready for use and designed to provide waterproofing and anti-corrosion protection of metal objects, porous surfaces and other building structures.
BKM 100 is a homogeneous compound based on petroleum bitumen, synthetic rubber, fillers and an organic solvent. This mixture of components forms a single semi-liquid consistency.
To create high-quality waterproofing, it is necessary to clean the work surface from dust, grease and other types of contamination. After that, the anti-corrosion mastic BKM 100 should be carefully placed, and then the composition should be laid using a brush, roller or spatula. The recommended thickness of the insulation layer is from 2 to 4 mm.
Specifications

• Water resistant for 72 hours at a pressure of 0.001 MPa
• Water absorption not more than 0.5% by weight
• Density at +20 °C 0.90 ± 10 g/cm3
• Heat resistance in 5 hours +75 °C
• Conditional tensile strength of 0.4 kgf/cm2
• Bending elasticity on a beam with a radius of 10 mm -15°C

BKM 200 is a bitumen–rubber mastic for cold use, which refers to waterproofing and anti-corrosion compounds, made from high-quality components, including petroleum bitumen, synthetic rubber and organic solvent. The composition of these components allows you to create a single homogeneous consistency that is ready for use and does not contain foreign inclusions, stains and lumps.
Bitumen mastic BKM 200 is endowed with high adhesion, excellent protective functions, resistance to moisture and deformation. In addition, the composition is characterized by optimal heat resistance, as well as resistance to precipitation.
The composition of the BKM 200 mastic is laid on the surface without preheating. The work surface is pre-cleaned, dried and primed. After that, using a construction brush or a spatula, the composition of the mastic is applied to the surface in 2-3 layers.
Specifications
Water resistant for 72 hours at a pressure of 0.001 MPa
Water absorption not more than 0.5% by weight
Density at +20 °C 0.90 ± 10 g/cm3
Heat resistance in 5 hours +75 °C
Conditional tensile strength of 0.4 kgf/cm2
Bending elasticity on a beam with a radius of 10 mm -15°C

Waterproofing mastic is designed to insulate and provide anti-corrosion protection for industrial facilities and commercial structures.
Specifications

• Viscosity according to B3-4 at +20 ° C 60-100 degrees.
• Adhesion strength to the substrate is not less than 0.1 MPa with concrete
• Heat resistance for 3 hours at least +50 ° C.
• Flexibility on a 10 mm diameter rod without cracking at -15 °C.
• The content of the pulverized filler is 15-20% by weight

Mastic KN 1 is a homogeneous composition made on the basis of chloroprene rubber, enriched with antioxidant, indencoumarone resin and diluted with an organic solvent.
Mastic is an adhesive rubber adhesive used as a substance for gluing:

• polyvinyl chloride floor coverings and rubber roll coverings;
• tile flooring, nitrolinoleum and parquet;
• profile mouldings and sealing sealing gaskets.

Adhesive rubber mastic, the price of which is favorable and affordable, refers to toxic compounds, therefore it is recommended to work with it using personal protective equipment.
Specifications

• Water absorption not more than 0.5% by weight
• Density at +20 °C from 0.90 to 10 g/m3
• Heat resistance in 5 hours +75°C
• Conditional tensile strength 72 hours
• Bending elasticity on a beam with a radius of 10 mm -15°C

Mastic KN 2 is a homogeneous viscous compound designed for gluing rubber floor materials (rubber linoleum and rubber tiles), and is also used for gluing sealing gaskets.
Rubber mastic KN 2 is a compound that is applied using a wide brush or a notched trowel to a previously cleaned and dry work surface. The adhesive composition is laid in layers, no more than 2 mm thick.
Specifications

• Viscosity according to B3-4 at +20 °C for the highest and I quality categories - from 2-9 Pa *s
• Adhesion strength to a steel surface in 1000 hours FOR THE HIGHEST QUALITY CATEGORY: at least 0.15 MPa 24 hours after gluing samples to a concrete base; at least 0.28 MPa 72 hours after gluing samples to a concrete base. FOR QUALITY CATEGORY I: at least 0.12 MPa 24 hours after gluing the samples to the concrete base; at least 0.24 MPa 72 hours after gluing the samples to the concrete base.
• The content of volatile components for the highest category is not more than 45%; for the first category of quality - not more than 50%

KN 3 mastic is used for gluing polyvinyl chloride linoleum, rubber coatings with a porous layer, nitrolinoleum, parquet boards, as well as profile mouldings. Due to its high adhesive ability, the KN 3 rubber mastic ensures reliable adhesion of the listed materials to the work surfaces.
Mastic KN 3, the price of which corresponds to the characteristics, is a composition that is applied to a pre-cleaned surface. A rigid construction brush or a notched trowel is used to lay the composition. Mastic is applied to surfaces and materials in layers. The optimal layer thickness is 2 mm.
Specifications

• Viscosity according to B3-4 at +20 °C for the highest and I quality categories - from 2-9 Pa *s
• Adhesion strength TO the substrate FOR THE HIGHEST QUALITY CATEGORY: at least 0.15 MPa 24 hours after gluing the samples to the concrete base; at least 0.28 MPa 72 hours after gluing the samples to the concrete base. FOR QUALITY CATEGORY I: at least 0.12 MPa 24 hours after gluing the samples to the concrete base; at least 0.24 MPa 72 hours after gluing the samples to the concrete base.
• The content of volatile components for the highest category is not more than 45%; for the first category of quality - not more than 50%

Kukersol mastic is a composition of the "cold" type of application, made on the basis of petroleum bitumen and varnish.
Kukersol cold mastic is used for waterproofing objects in order to protect them from corrosion and mechanical damage. In addition, mastic is used to seal cracks and seams on surfaces, and also finds its application in roofing, when gluing rolled roofing materials.
Kukersol cold mastic creates high-quality waterproofing and performs all operational properties when applied to a surface cleaned and primed. Before laying on the work site, it is recommended to thoroughly mix the composition, and then apply it to the surface using a brush or roller. Mastic should be applied in layers, because this technology of laying allows you to provide a high-quality coating with excellent performance properties.
Specifications

• Water absorption within 24 hours is not more than 5% by weight
• Elongation at break of at least 60%
• The bond strength to the substrate is not less than 1.5 MPa with concrete
• The softening temperature in KISH is at least from 65 ° C to +75 ° C.
• Heat resistance in 5 hours +70 ° C.
• Nominal strength 0.6 MPa
• Flexibility on a 10 mm diameter rod without cracking at -10 °C.

Latex mastic is a one-component cold-curing compound that is made from dispersed bitumen enriched with emulsifiers and latex.
Excellent waterproofing and protective properties, resistance to excessive moisture, corrosion and other negative external influences are the main advantages of bitumen latex mastic, which can be purchased on our website. In addition, the composition of the mastic is able to create a wear-resistant coating, which allows not only to increase the service life of the treated area, but also to provide it with optimal thermal insulation.
Specifications

• Adhesion strength to the substrate is 0.1 MPa with concrete
• Operating temperature range from 0 to + 30 ° C.
• Heat resistance for 5 hours at least +30 ° C.
• Flexibility on a 10 mm diameter rod without cracking at a temperature of -15 °C.
• The content of the pulverized filler is 0 % by weight